PVC Transparent Fabric for Equipment Bag Panels
A glossy clear PVC film laminate with woven polyethylene reinforcement for transparent bag panels.
- Weight
- 490gsm
- Width
- 1.05-3.2m
Product images
TECHNICAL DATASHEET
| Technology: | Lamination |
|---|---|
| Structure: | High Density Woven Polyethylene base fabric + clear PVC film / 3 layers laminated |
| Surface: | Glossy |
| Colour: | White/Blue/Green |
| Base fabric | 1000D 9*9 |
| Weight: | 490gsm |
| Width: | 1.05-3.2m |
| Roll length: | 50m |
| Packing: | Paper tube+PE film+Craft paper |
| MOQ: | 3000yards for customization/ 100yards for in-stock |
APPLICATIONS:
Product Features
- Woven reinforcementA woven polyethylene grid reinforces the clear PVC laminate.
- Glossy clear faceA glossy PVC film gives the reinforced laminate a clear surface.
Clear Film And A 9×9 Base
DLT-6906 combines continuous clear PVC film with a visible woven base. The 9×9 notation concerns the reinforcement arrangement, and 1000D concerns yarn size. Neither value is a transparency percentage or a finished tensile result. Examine a full colour swatch when specifying equipment viewing panels, since yarn coverage, colour and glossy surface reflections all contribute to the view through the material.
A Glossy Laminated Surface
The specified process is lamination, with a glossy exposed finish. Conversion should preserve the bond at bends and seams, particularly around small corners in a bag pattern. A trial should use the intended production colour and the planned joining method. Check the panel after folding and opening it, then inspect the edges where cutting exposes the composite construction to handling.
Application requirements — Clear Reinforced Bags
Specify window or panel dimensions, thickness, viewing requirements, framing and the normal folding or rolling pattern. Review optical appearance, flexibility, surface marking and the edge or seam construction. Confirm the temperature range, cleaning method and any specified fire behaviour on the selected grade.
Finished Clear-Bag Configurations
Clear reinforced PVC can be converted into flat document pouches or gusseted carry bags. Define the usable space separately from the outside dimensions.
| Specification | Configuration |
|---|---|
| Document-Pouch Example | 330 × 240 mm outside; 325 × 235 mm usable interior |
| Carry-Bag Example | 12 × 12 × 6 in, stated as width × height × depth |
| Body Shape | Flat two-panel pouch or a bag with a base and side gussets |
| Closure | Zipper at the opening, with end stops and a usable pull |
| Handle Example | 1.5 in webbing carry handles on the gusseted configuration |
| Clear Area | Position print and labels to leave the required contents visible |
| Fabrication Sample | Check the zipper opening, seams and fit with the intended contents |
| Order Drawing | State outside dimensions, usable space, gusset depth and handle positions |
Construction Details
Flat Pouch And Gusseted Bag
A flat pouch suits documents. A gusset adds depth for bulkier contents; include that depth when stating the bag size.
Opening And Carry Points
Locate zipper ends clear of the handle attachments. Confirm the finished handle connection on a sewn sample.
Product Videos 2 videos
Clear Reinforced Fabric: Production and Samples
Production & Material Footage
Discuss the application.
For PVC transparent fabric rolls, specify the panel colour, equipment viewing needs and the finished bag edge design.
PVC Transparent Fabric With A Visible Reinforcing Base
DLT-6906 is PVC transparent fabric constructed from clear PVC film and a woven polyethylene base. The specification describes a three-layer laminate with a glossy surface. The reinforcement is part of the finished composite, so a completed bag panel will show a grid through the film. Its visual effect depends on the chosen colour and the background behind it, as well as the lighting used to inspect the sample.
The base is specified as 1000D with a 9×9 construction notation. Finished weight is 490gsm, and white, blue and green are listed colour choices. These are sheet specifications, not a statement that every panel has the same visible transparency. Ask to compare the actual colour sample at the size of the intended pocket, especially when the user needs to identify tools or equipment through it.
During lamination, the film and reinforcing base are combined into a composite. A reliable bond allows the layers to bend together through subsequent cutting and fabrication. The glossy film also makes reflections and handling marks more noticeable during inspection. Keep a flat reference swatch alongside a fabricated sample to distinguish the original surface appearance from changes introduced by a seam or fold.
DLT-6906 is supplied in the listed 1.05-3.2m width range and 50m roll length. For equipment bag panels, identify the reinforcement directions on the pattern and review the load paths around handles and closures. The bag construction should carry those loads through suitable seams and edge details; the transparent sheet specification alone does not define a finished bag load rating.